沙伯基础创新PC LEXAN EXL9330 产品特性及用途：无卤防火，5VA阻燃，耐低温－40℃，韧性好，抗紫外线，良好的可加工性，瓷白，用于手机外壳和低温寒冷使用产品
我公司提供的产品均为正牌塑胶原料，品质保证，货源稳定，送货上门，可免费提供官方物性表、UL黄卡，并随货提供RoHS报告、SGS报告等，索取权威资料请致电13268582149
PC EXL9330 物性表：
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.80 | % | Internal Method |
| Molding Shrinkage - Across Flow (3.20 mm) | 0.40 to 0.80 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 0.35 | % | ISO 62 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus 2 | 2100 | MPa | ASTM D638 |
| Tensile Modulus | 2100 | MPa | ISO 527-2/1 |
| Tensile Strength 3 (Yield) | 58.6 | MPa | ASTM D638 |
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strength 3 (Break) | 61.4 | MPa | ASTM D638 |
| Tensile Stress (Break) | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation 3 (Yield) | 6.0 | % | ASTM D638 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Tensile Elongation 3 (Break) | 130 | % | ASTM D638 |
| Tensile Strain (Break) | 130 | % | ISO 527-2/50 |
| Flexural Modulus 4 (50.0 mm Span) | 2070 | MPa | ASTM D790 |
| Flexural Modulus 5 | 2200 | MPa | ISO 178 |
| Flexural Strength 5, 6 | 85.0 | MPa | ISO 178 |
| Flexural Strength 4 (Yield, 50.0 mm Span) | 88.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength 7 | ISO 179/1eA | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 75 | kJ/m² | |
| Charpy Unnotched Impact Strength 7 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | ASTM D256 | ||
| -50°C | 590 | J/m | |
| -30°C | 680 | J/m | |
| 23°C | 800 | J/m | |
| 23°C, 6.40 mm | 640 | J/m | |
| Notched Izod Impact Strength | |||
| -30°C 8 | 55 | kJ/m² | ISO 180/1A |
| -30°C 9 | 65 | kJ/m² | ISO 180/4A |
| 23°C 8 | 70 | kJ/m² | ISO 180/1A |
| 23°C 9 | 80 | kJ/m² | ISO 180/4A |
| Unnotched Izod Impact 10 (23°C) | 1100 | J/m | Internal Method |
| Unnotched Izod Impact Strength 8 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 52.9 | J | ASTM D3763 |
| Hardness | Nominal Value | Unit | Test Method |
| Ball Indentation Hardness (H 358/30) | 90.0 | MPa | ISO 2039-1 |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 134 | °C | ASTM D648 |
| Heat Deflection Temperature 11 (0.45 MPa, Unannealed, 100 mm Span) | 135 | °C | ISO 75-2/Be |
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 121 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 124 | °C | |
| Heat Deflection Temperature 11 (1.8 MPa, Unannealed, 100 mm Span) | 124 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 142 | °C | ASTM D1525 12 |
| Vicat Softening Temperature |