防火阻燃PA9T 高温尼龙G2450 日本可乐丽PA9T
填料/增强材料/玻璃纤维增强材料,45%填料按重量,耐温285度防火VO
|
性能项目
|
测试条件
|
测试方法
|
数值/描述
|
单位
|
|
|
机械性能
|
拉伸强度(引张强度)
|
ASTM D638/ISO 527
|
190
|
kg/cm²(MPa)[Lb/in2]
|
|
|
断裂伸长率
|
ASTM D638/ISO 527
|
2.7
|
%
|
||
|
拉伸模量
|
ASTM D638/ISO 527
|
kg/cm²(MPa)[Lb/in2]
|
|||
|
拉伸屈服伸长率(延伸率)
|
ASTM D638/ISO 527
|
%
|
|||
|
拉伸断裂伸长率(延伸率)
|
ASTM D638/ISO 527
|
14
|
%
|
||
|
弯曲模量(弯曲弹性率)
|
ASTM D790/ISO 178
|
kg/cm²(MPa)[Lb/in2]
|
|||
|
弯曲强度
|
ASTM D790/ISO 178
|
240
|
kg/cm²(MPa)[Lb/in2]
|
||
|
洛氏硬度
|
ASTM D785
|
||||
|
IZOD 缺口冲击强度
|
1/4" -30℃
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
||
|
1/4" 23℃
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
|||
|
1/8" 23℃
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
|||
|
1/8" -30℃
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
|||
|
Charpy冲击强度
|
23℃ （缺口）
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
||
|
-30℃（缺口）
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
|||
|
23℃（无缺口）
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
|||
|
-30℃（无缺口）
|
ASTM D256/ISO 179
|
kg·cm/cm(J/M)ft·lb/in
|
|||
|
物性性能
|
比重（密度）
|
ASTM D792/ISO 1183
|
1.77
|
||
|
成型收缩率
|
ASTM D955
|
0.1
|
%
|
||
|
熔融指数（流动系数）
|
200℃/5kg
|
ASTM D1238/ISO 1133
|
g/10min
|
||
|
220℃/10kg
|
ASTM D1238/ISO 1133
|
g/10min
|
|||
|
吸水率 23℃/24H
|
ASTM D570/ISO 62
|
%
|
|||
|
热性能
|
热变形温度
|
退火
|
ASTM D648/ISO 75
|
℃（℉）
|
|
|
未退火
|
ASTM D648/ISO 75
|
℃（℉）
|
|||
|
维卡软化点
|
ASTM D1525/ISO R306
|
℃（℉）
|
|||
|
熔点
|
-
|
℃（℉）
|
|||
|
燃烧性（率）
|
UL94
|
||||
|
线性膨胀系数
|
ASTM D696/ISO 11359
|
||||
|
电气性能
|
介电常数
|
100HZ
|
ASTM D150/IEC 60250
|
||
|
1MHZ
|
ASTM D150/IEC 60250
|
||||
|
体积电阻率
|
ASTM D257/IEC 60093
|
Ω.cm
|
|||
|
表面电阻率
|
ASTM D257/IEC 60093
|
Ω
|
|||
|
加工条件
|
干燥条件
|
||||
|
加工温度
|
射嘴
|
℃
|
|||
|
料筒前段
|
℃
|
||||
|
料筒中段
|
℃
|
||||
|
料筒后段
|
℃
|
||||
|
熔体温度
|
℃
|
||||
|
模具温度
|
℃
|
||||
|
压力
|
注塑压力
|
Mpa
|
|||
|
保压压力
|
Mpa
|
||||
|
背压
|
Mpa
|
||||
|
螺杆转速
|
rpm
|
||||
|
其他
|
备注
|
||||
|
颜色
|
|||||
|
特性
|
高强度
|
||||
|
用途
|
电子电器行业系统酌配件。
|
||||